Delrin? 527UV NC010
ACETAL RESIN
產品說明:
UV Stabilized Medium Viscosity Acetal Homopolymer
添加劑 | |
特性 | |
RoHS 合規(guī)性 | |
形式 | |
加工方法 | |
多點數據 | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Shear Modulus vs. Temperature, Dynamic (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Tensile Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)
|
部件標識代碼 (ISO 11469) | |
樹脂ID (ISO 1043) | |
密度 | 1.42 | g/cm3 | ISO 1183 |
熔流率（熔體流動速率） | 15 | g/10 min | ISO 1133 |
熔融體積流量（MVR） (190°C/2.16 kg) | 0.793 | in3/10min | ISO 1133 |
收縮率 |
|
| ISO 294-4 |
橫向流量 | 1.9 | % |
|
流量 | 2.0 | % |
|
吸水率 |
|
| ISO 62 |
73°F, 24 hr | 0.50 | % |
|
飽和, 73°F, 0.0787 in | 1.2 | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 0.20 | % |
|
洛氏硬度 |
|
| ISO 2039-2 |
M 計秤 | 92 |
|
|
R 計秤 | 120 |
|
|
拉伸模量 | 450000 | psi | ISO 527-2 |
拉伸應力 (屈服) | 10200 | psi | ISO 527-2 |
拉伸應變 (屈服) | 17 | % | ISO 527-2 |
標稱拉伸斷裂應變 | 30 | % | ISO 527-2 |
彎曲模量 | 435000 | psi | ISO 178 |
彎曲應力 |
|
| ISO 178 |
-- | 11200 | psi |
|
3.5% 應變 | 11300 | psi |
|
泊松比 | 0.37 |
| ISO 527 |
簡支梁缺口沖擊強度 |
|
| ISO 179/1eA |
-22°F | 3.8 | ft·lb/in2 |
|
73°F | 4.3 | ft·lb/in2 |
|
簡支梁無缺口沖擊強度 |
|
| ISO 179/1eU |
-22°F | 120 | ft·lb/in2 |
|
73°F | 120 | ft·lb/in2 |
|
懸壁梁缺口沖擊強度 |
|
| ISO 180/1A |
-40°F | 3.8 | ft·lb/in2 |
|
73°F | 3.8 | ft·lb/in2 |
|
熱變形溫度 |
|
|
|
66 psi, 未退火 | 325 | °F | ISO 75-2/B |
264 psi, 未退火 | 203 | °F | ISO 75-2/A |
維卡軟化溫度 |
|
|
|
-- | 345 | °F | ISO 306/A50 |
-- | 320 | °F | ISO 306/B50 |
熔融溫度 3 | 352 | °F | ISO 11357-3 |
線形熱膨脹系數 |
|
| ISO 11359-2 |
流動 | 6.1E-5 | in/in/°F |
|
橫向 | 6.7E-5 | in/in/°F |
|
Annealing Time - Optional | 30.0 | min/mm |
|
退火溫度 | 320 | °F |
|
表面電阻率 | 2.0E+13 | ohms | IEC 60093 |
體積電阻率 | > 1.0E+15 | ohms·cm | IEC 60093 |
相對電容率 |
|
| IEC 60250 |
100 Hz | 3.80 |
|
|
1 MHz | 3.80 |
|
|
耗散因數 |
|
| IEC 60250 |
100 Hz | 2.1E-3 |
|
|
1 MHz | 5.6E-3 |
|
|
漏電起痕指數 | 600 | V | IEC 60112 |
燃燒速率 4 (0.0394 in) | 0.83 | in/min | ISO 3795 |
UL 阻燃等級 |
|
|
|
0.031 in | HB |
| UL 94 |
0.03 in | HB |
| IEC 60695-11-10, -20 |
FMVSS 可燃性 | B |
| FMVSS 302 |
霧化 |
|
| ISO 6452 |
F-value (refraction) 5 | 90 | % |
|
G-value (condensate) | 2.0E-4 | g |
|
Emission | < 8.00 | mg/kg | VDA 275 |
干燥溫度 | 176 | °F |
|
干燥時間 - 熱風干燥機 | 2.0 到 4.0 | hr |
|
建議的最大水分含量 | 0.20 | % |
|
加工（熔體）溫度 | 410 到 428 | °F |
|
Melt Temperature, Optimum | 419 | °F |
|
模具溫度 | 176 到 212 | °F |
|
Mold Temperature, Optimum | 194 | °F |
|
保壓 | 11600 到 14500 | psi |
|
Drying Recommended | yes |
|
|
Hold Pressure Time | 8.00 | s/mm |
|
如需杜邦（DUPONT）原廠物性表及相關文件，請聯系我們工作人員，謝謝！